Dry sliding wear behavior of the reinforced by graphite particle and heat treated of recycled aluminum AA6061 based MMC fabricated by powder metallurgy method

Mahdi, Ahmed Sahib and Mustapa, Mohd Sukri and Mohamad, Mahmod Abd Hakim and M. Tobi, Abdul L. and Ab Kadir, Muhammad Irfan and Samsi, Mohd Arif (2017) Dry sliding wear behavior of the reinforced by graphite particle and heat treated of recycled aluminum AA6061 based MMC fabricated by powder metallurgy method. Key Engineering Materials, 740 . pp. 9-16. ISSN 16629795

Full text not available from this repository.

Official URL: doi:10.4028/www.scientific.net/KEM.740.9

Abstract

The micro-hardness and compression strength of recycling aluminum alloy AA6061 were investigated as a function of the different microstructure and constituent powder metallurgy method. Five specimens with various fabrication parameters were selected to investigate the compression strength and microhardness. The first, as fabricated specimen (as compacted), the second was as heat treated by quenching and aging process. Three specimens were mixed with Graphite particles as a reinforcement material. Compression strength values were tested for the specimens as fabricated and heat treated which were 195 and 300 MPa, respectively. The improvement ratio was 52% for the specimen as heat treated. On the other hand, high wear resistance was given by the specimen as heat treated, whereas, the lower wear strength was at the specimen mixed with 4.5% Graphite. These results were attributed to that the wear resistance related to the microhardness value.

Item Type:Article
Uncontrolled Keywords:Recycling aluminum; heat treatment process; milling process; powder metallurgy; AA6061
Subjects:T Technology > TS Manufactures > TS200-770 Metal manufactures. Metalworking
Divisions:Centre of Diploma Studies > Department of Mechanical Engineering
ID Code:11084
Deposited By:Mr. Mohammad Shaifulrip Ithnin
Deposited On:13 May 2019 09:08
Last Modified:13 May 2019 09:08

Repository Staff Only: item control page