Electrophoretic deposited LSCF-SDCC-Ag cathode coating on ferritic stainless steel interconnect for SOFC

Omar, Noor Irinah and Kang, Huai Tan and Taib, H. and Abd. Rahman, Hamimah (2018) Electrophoretic deposited LSCF-SDCC-Ag cathode coating on ferritic stainless steel interconnect for SOFC. Journal of Physics: Conference Series, 1082 (1). pp. 12-28. ISSN 1742-6588

Text AJ 2018 (1018) Electrophoretic deposited LSCF-SDCC-Ag cathode coating on ferritic stainless steel interconnect for SOFC.pdf Restricted to Registered users only Download (1MB) | Request a copy

Abstract

The application of electrophoretic deposition (EPD) technique in development of composite cathode as a coating layer on ferritic stainless steel (FSS) interconnect for solid oxide fuel cell (SOFC) has acquired a great interest. The aim of this study is to determine the capability of EPD technique in producing composite cathode coating. The lanthanum strontium cobalt ferrite (LSCF)-samarium doped ceria carbonate (SDCC) composite cathode powder with silver (Ag) addition was fabricated adopting the EPD technique. LSCF-SDCC-Ag suspension was prepared by using organic-aqueous solvent for the deposition. The coated FSS substrate was first heat treated at 600°C for 90 minutes in air. The deposition was carried out at different applied voltages (5, 7 and 10 volt) and deposition durations (5-20 minutes). The increment of applied voltage and deposition duration was found to contribute to the increment of LSCF-SDCC-Ag deposited weight. The highest deposited weight and thickness of coating was 2.47 mg/cm² and 62.73 µm respectively attained by deposition of 10 volt for 20 minutes. According to the obtained results, deposition at 10 volt within 5 to 20 minutes has shown a better deposition. It is thus clear that EPD is indeed a feasible technique applicable for the development of composite cathode for SOFC interconnects and yielded better coating thicknesses of LSCF-SDCC-Ag on FSS interconnect for SOFC.

Item Type:	Article
Subjects:	T Technology > TK Electrical engineering. Electronics Nuclear engineering > TK7800-8360 Electronics T Technology > TS Manufactures > TS200-770 Metal manufactures. Metalworking
Divisions:	Faculty of Mechanical and Manufacturing Engineering > Department of Manufacturing Engineering
Depositing User:	UiTM Student Praktikal
Date Deposited:	26 Jan 2022 04:28
Last Modified:	26 Jan 2022 04:28
URI:	http://eprints.uthm.edu.my/id/eprint/6066

Actions (login required)

View Item