PHYSICAL CHARACTERIZATION OF POLYURETHANECLAY COMPOSITE DOPED WITH TREATED AND UNTREATED PU WASTE AS FILLER FOR SUBGRADE LAYER APPLICATIONS

Atil, Aida Atiqah and Mat Hassan, Nik Normunira and Roseli, Adyla Illyana and Mohamed Yusop, Fatimah and Mohd Rus, Anika Zafiah and Marsi, Noraini and Tuan Ismail, Tuan Noor Hasanah and Yahya, Nur Faezah (2023) PHYSICAL CHARACTERIZATION OF POLYURETHANECLAY COMPOSITE DOPED WITH TREATED AND UNTREATED PU WASTE AS FILLER FOR SUBGRADE LAYER APPLICATIONS. Malaysian Construction Research Journa, 39 (1). pp. 29-40.

[img] Text
J16003_c17cd4cd70a470ade625b1d057ae1696.pdf
Restricted to Registered users only

Download (651kB) | Request a copy

Abstract

One of the most efficient ways to enhance the geotechnical characteristics of soils is to use polyurethane waste as a filler. In this study, the PU waste was soaked in a 0.05 M sodium hydroxide (NaOH) solution as an alkaline cleaner before being sieved to a size of 300 m. Then, the PU waste as filler was dried in microwaves and a drying oven. The PU clay composite samples were prepared at 0%, 2.5%, and 5% of PU waste filler loading namely PU waste untreated (PU-CCUn), PU waste treated by microwave (PU-CCTW), and PU waste treated by the oven (PU-CCTO), respectively. Fourier Transform Infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and water absorption was used to examine the physical characteristics of PU clay composite with treated and untreated PU waste filler loading. According to the results, the functional group of PU clay composite samples shows no significant changes with the drying treatment. However, from SEM image exhibited the PU waste particle was mixed successfully in clay. The PU clay composite shows that 12% more water was absorbed by PU-CCUn than by PU-CCTO and PU-CCTM due to the bigger pore sizes. In summary, the risk of overheating and burning the PU waste as filler powder with the microwave processing method makes the prospective PU-CCTO the best potential in comparison to PU-CCUn and PU-CCTM. This demonstrated the effectiveness of the drying oven treatment method and its superior wettability to that of the microwave. In the future, it is recommended to utilize PU waste as filler that has been dried at a variable ratio of up to 10%.

Item Type: Article
Uncontrolled Keywords: PU Filler; Polyurethane Waste; Drying; Subgrade Layer.
Subjects: T Technology > T Technology (General)
Divisions: Faculty of Engineering Technology > Department of Mechnical Engineering Technology
Depositing User: Mr. Mohamad Zulkhibri Rahmad
Date Deposited: 17 Jul 2023 07:40
Last Modified: 17 Jul 2023 07:40
URI: http://eprints.uthm.edu.my/id/eprint/9220

Actions (login required)

View Item View Item