Woven fabric carbon fibre composites hybrid joints under quasi-static testing

Lee, S. Y. and Ahmad, H. (2018) Woven fabric carbon fibre composites hybrid joints under quasi-static testing. Journal of Advanced Manufacturing Technology, 12 (1). pp. 13-24. ISSN 22898107

Full text not available from this repository.

Abstract

Twill weave carbon fibre reinforced polymer (CFRP) hybrid adhesively bonded-bolted joints was investigated on bearing stress at failure in experimental programmes. The present paper comprises effects of joint type, normalised coupon width (W/d), laminate orientations and bolt load as specified in designed series. All CFRP hybrid joints exhibited cohesive failure before ultimate failure i.e., net-tension and bearing/net-tension failures. Bearing stress at failure was found to increase with normalized W/d and small W/d led to net-tension failure occurrence. Double-lap joints (DLJs) were stronger than single-lap joints (SLJs) due to secondary bending phenomenon in SLJs. Cross-ply presented greater strength than quasiisotropic lay-up caused by the presence of 0˚ fibres orientation. Clamped condition (applied torque, T = 5 Nm) may change the critical W/d than finger-tight (FT) case as net-tension failures is likely to occur under clamped condition.

Item Type: Article
Uncontrolled Keywords: Hybrid joints; woven fabric; CFRP; failure modes; bearing stress
Subjects: T Technology > TH Building construction > TH845-895 Architectural engineering. Structural engineering of buildings
Divisions: Faculty of Civil and Environmental Engineering > Department of Structural and Material Engineering
Depositing User: Mr. Mohammad Shaifulrip Ithnin
Date Deposited: 31 Mar 2019 07:35
Last Modified: 31 Mar 2019 07:35
URI: http://eprints.uthm.edu.my/id/eprint/11247
Statistic Details: View Download Statistic

Actions (login required)

View Item View Item