Surface morphology and bond characterization of nanocrystalline diamonds grown on tungsten carbide via hot filament chemical vapor deposition

Hamzah, E. and Yong, Tze Mi and Mat Yajid, M. A. (2013) Surface morphology and bond characterization of nanocrystalline diamonds grown on tungsten carbide via hot filament chemical vapor deposition. Journal of Crystal Growth, 372. pp. 109-115. ISSN 0022-0248

[img]
Preview
PDF
dr_yong_tze_mi_2.pdf

Download (1MB)

Abstract

Nanocrystalline diamonds (NCDs) were deposited on chemically prepared tungsten carbide substrates via hot filament chemical vapor deposition. The surface morphology of the NCDs was examined using field emission scanning electron microscopy. The NCDs formed a ballas morphology evenly across the tungsten carbide surface. Overetching affected the diamond deposition by causing the ballas to form aggregations. Cross-sectional fragmentation using a diamond wafering blade caused the nanocrystalline diamond to fragment at overetched boundaries, and delamination only occurred 30–50 µm off the edge and revealed that the thickness of the diamond film was 6 µm. Grazing XRD is an effective method to identify diamonds even at the nanoscale. The crystallite size was calculated to be 18.4 nm by modeling. Cross-sectional TEM analysis indicated that the diamond grain size was approximately 10–30 nm near the interface. Amorphous carbon, an embedded diamond and voids were also observed. TEM also revealed that the tungsten carbide surface undulates. The nanocrystalline diamonds nucleated and grew on the tungsten carbide (100) planes in the 〈111〉 direction, forming (111) planes, as observed from HRTEM, d-spacing measurements, SAD and FFT analyses for a FIB-prepared sample.

Item Type: Article
Uncontrolled Keywords: crystal morphology; interfaces; diamond; nanomaterials
Subjects: T Technology > TA Engineering (General). Civil engineering (General) > TA401-492 Materials of engineering and construction. Mechanics of materials
Divisions: Faculty of Engineering Technology > Department of Mechanical Engineering Technology
Depositing User: Normajihan Abd. Rahman
Date Deposited: 07 Aug 2016 08:48
Last Modified: 07 Aug 2016 08:48
URI: http://eprints.uthm.edu.my/id/eprint/8204