Muhammad, Nur Ainnaa Mardhiah and Awang, Noor Azura and Nik Mahmud, Nik Noor Haryatul Eleena and Zalkepali, Noor Ummi Hazirah Hani and Muhamad Zamri, Ain Zamira and Basri, Hatijah and Rasli, Nurul Izwanie (2023) Biosynthesized zinc oxide and titanium dioxide nanoparticles by aloe vera extract for tunable Q-switched application. Optical Fiber Technology, 77. pp. 1-8.
![]() |
Text
J15903_30467d566ac259b483400d4ec79f2600.pdf Restricted to Registered users only Download (5MB) | Request a copy |
Abstract
Zinc oxide (ZnO) and titanium dioxide (TiO2) nanoparticles (NPs) were biosynthesized by using aloe vera extract for tunable Q-switched application. ZnO TiO2 NPs was then prepared as a saturable absorber (SA) via mechanical exfoliation technique. By measuring nonlinear optical absorption, the modulation depth and saturation intensity were 1.57 % and 0.05 MW/cm , respectively. The obtained output pulse had a 1567.60 nm central wavelength and a signal-to-noise ratio (SNR) of 44.94 dB at a pump power of 248.50 mW. The increase of pump power from 178.00 mW to 248.50 mW has led to continuously increase in the repetition rate from 7.70 kHz to 12.99 kHz and decrease from 45.35 µs to 28.93 µs of pulse width, respectively. At maximum pump power, 5.06 nJ of pulse energy was also recorded. When the tunable bandpass filter (TBF) was incorporated into the cavity, the wavelength-tunable Q-switched pulses was constructed, and the tuning wavelength from 1530 nm to 1570 nm that of 40 nm covering wavelength was attained. This finding suggests that a wider range of tunable and simple designs is applicable to optical communications and sensing applications.
Item Type: | Article |
---|---|
Uncontrolled Keywords: | - |
Subjects: | T Technology > T Technology (General) |
Divisions: | Faculty of Applied Science and Technology > FAST |
Depositing User: | Mr. Mohamad Zulkhibri Rahmad |
Date Deposited: | 01 Aug 2024 02:51 |
Last Modified: | 01 Aug 2024 02:51 |
URI: | http://eprints.uthm.edu.my/id/eprint/11445 |
Actions (login required)
![]() |
View Item |