Study of physio-mechanical properties of refractory fireclay for production of furnace lining

Job Ajala, Amkpa and Badarulzaman, Nur Azam (2018) Study of physio-mechanical properties of refractory fireclay for production of furnace lining. Advanced Science Letters, 24 (6). pp. 3940-3944. ISSN 1936-6612

Full text not available from this repository. (Request a copy)

Abstract

This study focused on the Gombe fireclay that is under-utilized despite its abundance as essential ingredient for the manufacture of refractories. Hence, the clay was studied and appraised for its appropriateness for the manufacture of refractory fireclay brick. The physical, mechanical and thermal properties were investigated according to ASTM Standard Test Methods for fireclay refractories. Its chemical composition result indicated that it belongs to alumino-silicate group. Its refractoriness proved that it is a high duty (siliceous) refractory brick with refractoriness of 1621 °C equivalent to PCE Segar cone 26. It was sintered at varied sintering temperatures of 900 °C, 1000 °C, 1200 °C and 1100 °C. The sintering temperature of 1200 °C was found to be the best which significantly influenced the mechanical properties. The cold crushing strength was 15.37 MPa, apparent porosity was 24.52%, firing shrinkage was 7.5% and the bulk density was 1.9 g/cm3. The experimental result proved that the clay was suitable for production of refractory fireclay brick for furnace lining.

Item Type: Article
Uncontrolled Keywords: Air Pores; Fireclay Brick; Raw Clay Material; Sintering Temperature
Subjects: T Technology > TP Chemical technology > TP785-869 Clay industries. Ceramics. Glass
Divisions: Faculty of Mechanical and Manufacturing Engineering > Department of Manufacturing Engineering
Depositing User: UiTM Student Praktikal
Date Deposited: 24 Jan 2022 07:03
Last Modified: 24 Jan 2022 07:03
URI: http://eprints.uthm.edu.my/id/eprint/5884

Actions (login required)

View Item View Item