Md Jalil, Mohd Azlis Sani (2005) Development of Al-Cu-SiCp metal matrix composite for automotive applications. Masters thesis, Universiti Malaya.
|
Text
24p MOHD AZLIS SANI MD JALIL.pdf Download (6MB) | Preview |
Abstract
In recent years, the demand for reduced weight and high performance materials for automotive applications such as brake disc have increased. The newly developed, aluminium metal matrix composite (AI-MMC) reinforced with silicon carbide (SiC) particulate seem suitable to be an alternative material for this application. In this experimental study, AI-Cu-SiCp MMC was developed through stir casting method with sand mould. A constant 4.5% of weight percentage of 5 !-Ull pure copper powder was added to the mixtures to enhance the properties of AI-MMC. The effects of particle sizes of SiC as well as the weight percentage of SiC, pouring temperature and stirring time on the hardness, wear, compressive properties, flexure behavior and density of Al�Cu-SiCp MMC were investigated. Taguchi's Robust Parametric Design was used \vith ilmer array L9 34 and outer array with 2 replications to plan the experimental runs. A statistical Pareto Analysis of Variance (Pareto ANOVA) was employed to detennine the significant factors of these properties and optimum combinations of process variables for targeted functions. From the analysis, it was found that particle sizes of SiC is the most significant factor for density characteristic and compressive properties while weight percentage of SiC is the most significant factor for hardness and wear resistance characteristics. Optimum combinations were determined and conformity test were conducted to verify the optimum properties of newly developed material, AI-Cu-SiCp MMC. Optimum combination of hardness was AIB2CoDO ( 59 fllll particle size af SiC, 15% af weight percentage af SiC, 675°C pauring temperature and 5 minutes stirring time) with 82.5 HV; wear rate A2B2C2Do ( 106 flm particle size af SiC, 15% af weight percentage af SiC, 725°C pauring temperature and 5 lllinutes stirring time) with 1.585 x 10-5 g/sec; compressive strength A1B2C2Dl (59 flm particle size of SiC, 15% afweight percentage af SiC, 725°C pouring temperature and 10 minutes stirring time) with 9410.06 MPa and density AoB1C1Dl ( 40 flm particle size af SiC, 10% af weight percentage of SiC, 700°C pauring temperature and 10 minutes stirring time) with 2.6592 g/cm3 •
Item Type: | Thesis (Masters) |
---|---|
Subjects: | T Technology > TL Motor vehicles. Aeronautics. Astronautics T Technology > TL Motor vehicles. Aeronautics. Astronautics > TL1-484 Motor vehicles. Cycles |
Depositing User: | Mrs. Sabarina Che Mat |
Date Deposited: | 08 Sep 2022 02:47 |
Last Modified: | 08 Sep 2022 02:47 |
URI: | http://eprints.uthm.edu.my/id/eprint/7672 |
Actions (login required)
![]() |
View Item |