Effect of reaction temperature on steam methane reforming’s yield over coated nickel aluminide (Ni3Al) catalyst in micro reactor

Madon, Rais Hanizam and Mas Fawzi, Mas Fawzi and Sarwani, Muhamad Khairul Ilman and Osman, S.A. and Razali, Mohd Azahari and Mohammad, Abdul Wahab (2018) Effect of reaction temperature on steam methane reforming’s yield over coated nickel aluminide (Ni3Al) catalyst in micro reactor. Journal of Advanced Research in Fluid Mechanics and Thermal Sciences, 50 (2). pp. 170-177. ISSN 2289-7879

Text AJ 2018 (945) Effect of reaction temperature on steam methane reforming’s yield over coated nickel aluminide (Ni3Al) catalyst in micro reactor.pdf Restricted to Registered users only Download (700kB) | Request a copy

Abstract

This work investigates the effect of reaction temperature on methane conversion and hydrogen yield over coated Nickel Aluminide (Ni3Al) as an intermetallic alloy catalyst in micro reactor. The Ni3Al was impregnated at micro scale using dip coating technique. The coating impregnation process, consist of a few stages which are substrates and solgel preparation, dip coating, calcination and reduction of oxide molecule. The coated Ni3Al were characterized by X-Ray Diffraction (XRD) and Temperature Programming Reduction (TPR) then activated using H2. The XRD and TPR results showed present of Ni3Al on the coated surface and was successfully activated at 500°C and 46 minutes. Meanwhile, the steam methane reforming with the catalytic reaction took place at temperature from 500°C to 700°C, steam to carbon ratio of 3:1 and 5 hours reaction time. The reaction temperature of 600°C obtained the highest methane conversion of 43% and hydrogen yield of 29%. The limitation point of reaction activity either as zero reaction or deactivation point was found at 500°C and 700°C. The coated Ni3Al showed catalytic activity for each reaction temperature and work accordingly on the heterogenous catalyst principal theory of lag, exponential, stationary and deactivation stage.

Item Type:	Article
Uncontrolled Keywords:	Dip coating; micro reactor; Methane conversion; Hydrogen yield; reaction temperature
Subjects:	T Technology > TJ Mechanical engineering and machinery T Technology > TJ Mechanical engineering and machinery > TJ255-265 Heat engines
Divisions:	Faculty of Engineering Technology > Department of Mechnical Engineering Technology
Depositing User:	UiTM Student Praktikal
Date Deposited:	25 Jan 2022 00:52
Last Modified:	25 Jan 2022 00:52
URI:	http://eprints.uthm.edu.my/id/eprint/5935

Actions (login required)

View Item